Product Description

AID PE F5 is a masterbatch containing 5% fluorinated copolymer based in a LLDPE carrier. It is used in LLDPE

film extrusion to reduce melt-fracture and sharkskin when extruding linear olefin polymers. AID PE F5 also gives

the following properties : improved bubble stability, haze reduction, improved gloss and higher output levels.

SPECIFICATIONS

Melt Index (190 °C / 2.16 kg)

2 -4

Fluropolymer content

4,5 -5,5 %

ADDITIONAL TYPICAL PROPERTIES

Appearance

Milky-White granules

Volatiles (105°C / 1 h)

< 1500 ppm

These 2 graphs figure according to the results of lab tests with 500 ppm of additives " Processing Aid".

Evolution of the die pressure vs time

112

114

116

118

120

122

124

126

128

130

132

134

0

5

1 0

1 5

2 0

2 5

3 0

3 5

4 0

4 5

5 0

Time (min)

Competition

A ID PE F2 /AID PE F5

% of Melt Fracture vs. time after introduction of PPA

masterbatch

0

10

20

30

40

50

60

70

80

90

100

0

10

20

30

40

50

60

70

80

90

100

Time (min.)

Competition

AID PE F2 /AID PE F5

Pressure (bars)

% of Melt FracturePolytechs s.a.s Z.I. de la gare – BP 14 – 76450 Cany Barville – France

Tél. +33(0)2 35 57 81 81 – Fax +33(0)2 35 57 81 92 - E-Mail : commercial@polytechs.fr

TVA FR 804 182 14003 – SIRET 418 214 003 000034 – Code APE 241 L – RC : Rouen 418 214 003

USAGE

AID PE F5 works by modifying the interface between the polymer melt and the metal surfaces of the extruder

barrel and die. The following is directions for start-up :

1/ the user must ensure all metal surfaces coming in contact with polymer are thoroughly cleaned so that they

become coated with fluoropolymer.

2/ Start-off by adding 10% AID PE F5 and 90% base polymer to pre-condition the extruder with fluoropolymer.

3/ After 15 - 20 minutes adjust extruder to full operating output speed and reduce AID PE F5 to approx. 1 - 2%.

Exact quantity depends on Machine, polymer type etc, however, polymer containing antiblock, pigments etc is

more abrasive, so more Polylube masterbatch is needed.

4/ Without a prolonged production interruption it should be possible to start-up without preconditioning the

extruder.

5/ If the extruder has been cleaned with an abrasive purging compound, start-up should be as above.

AID PE F5 has a favourable effect on viscous molten polymers during extrusion and injection. It is also used in

HDPE injection molding.

AID PE F5 is not recommended if temperatures > 240°C .

RECOMMENDED ADDITION RATES

Use concentrations of AID PE F5 in LLDPE blown film are between 0,5 and 1,5%.